Enhancement of Physical Appearance, Skin Permeation, and Odor Reduction Using Liposome of Hydrolyzed Salmon Collagen for Cosmetic Products

Hydrolyzed collagen (HC) derived from salmon (Oncorhynchus nerka) skin possesses properties that can nourish the skin, and it is one of the active ingredients used in cosmeceutical products for moisturizing the facial skin. However, HC solution gives off a fishy odor and it is gray in color that makes the product unacceptable for cosmetic purposes. This study aimed to use liposome-encapsulated hydrolyzed salmon collagen to improve its physical appearance, skin permeation, and eliminate the fishy odor. Two percent of HC and vitamin B3 (VitB3) were used as active ingredients to incorporate into liposomes. Phosphatidylcholine, cholesterol, and Tween 80 at a suitable weight ratio of 8 : 2 : 1 produced nano-sized vesicles (170.6 ± 0.70 nm) with the highest percentage of entrapment efficiency (95.72 ± 2.00%) of VitB3 and (49.63 ± 1.74%) of HC. Skin permeation and odor detection of the HC-VitB3 liposome were studied using Franz's diffusion cell and gas chromatography, respectively, and compared with HC-VitB3 solution. Subsequently, facial serums were formulated using HC-VitB3 liposomes and HC-VitB3 solutions, and a product satisfaction test was conducted with 100 volunteers to determine their preferred product. The results of the studies of HC-VitB3 liposome serum showed improved formulation appearance, enhanced skin permeation, and better odor elimination compared to the HC-VitB3 serum. Furthermore, seventy-three volunteers in the product satisfaction test preferred and selected the liposomal serum for its superior scent. From all the experimental results, it could be seen that liposomes can help increase skin penetration, and undesirable odors and colors can be masked by the appropriate lipid bilayer structure of liposomes.


Introduction
Collagen constitutes a substantial group of fbrous proteins located outside the cell, most commonly present in the bodies of both humans and animals.It comprises approximately 30% of all connective tissues in animals and ranks highest in terms of relative organ weight [1].For instance, it is found in 70-80% of the skin [2].Collagen is a substance that the body can naturally produce.Troughout our lives, there is a continuous process of synthesizing new collagen to replace the old collagen that has deteriorated.However, this process becomes imbalanced as we age because the degradation of collagen outpaces its production.Marine collagens, which can be obtained from invertebrate marine animals or fsh ofer several advantages, including a high yield and no risk of disease transmission [3].Hydrolyzed collagen (HC), particularly the one sourced from fsh skin or scales, has garnered attention as a promising source of biologically active peptides.It has also received recognition as a Kosher and Halal product, making it widely accepted [4].In this study, HC from salmon skin was provided by the International Center of Excellence in Seafood Science and Innovation, Faculty of Agro-Industry, Prince of Songkla University, Tailand.Fat-free HC powder was produced through the optimization of a one-step hydrolysis process using mixed proteases (papain and alcalase) [4].Te molecular weight (MW) distribution of defatted HC from salmon skin, representing proteins or peptides was in the range of 102-10,175 Da [5].Moreover, the HC powder exhibited a reduced fshy odor and a decrease in lipid oxidation products, making it a potential candidate for use in cosmetic products [4,5].However, despite the solubilization of the defatted HC powder in water to form a solution, a persistent fshy odor remained, and even intensifed over an extended period.Terefore, the utilization of liposomes to encapsulate hydrolyzed salmon collagen ofers an innovative and promising approach to enhance the quality of cosmetic products.Furthermore, to formulate an efective, nourishing, and synergistic cosmetic product, vitamin B3 (VitB3) or nicotinamide was utilized as one of the active ingredients in liposome serum.VitB3 plays a crucial role in enhancing collagen production, regulating the excessive deposition of glycosaminoglycans, and preventing protein glycation.Glycation can lead to the crosslinking of collagen and elastin molecules, resulting in skin stifness and rigidity, consequently altering the skin's viscoelastic properties [6].Moreover, VitB3 contributes to improved skin radiance, thereby expanding the potential for developing a successful and benefcial product within the cosmetic market.
Liposomes are small particles ranging from nanometers to micrometers in size.Tey appear as spherical vesicles containing natural or synthetic phospholipids, organized in a double-layered structure known as a lipid bilayer.Tis molecular structure comprises both a polar (hydrophilic) part and a nonpolar (hydrophobic) part.Tis structural arrangement enables liposomes to transport substances that are polar, nonpolar, or amphiphilic.Te distribution of these substances within the liposome vesicles depends on their solubility and hydrophobicity.Soluble molecules are typically located within the central cavity of the liposome, while hydrophobic molecules are located within the carbon chain of lipid bilayer [7].Liposomes can aid in diminishing the undesired odor associated with various drugs, substances, or extracts.A former study utilized fsh oil as an ingredient in bread production prepared in the form of liposomes to reduce the fsh oil odor [8].Furthermore, liposomes can assist in masking the color of various substances which are encapsulated within the vesicles [9,10].Liposomes are even used for textile and engineering applications, where moringa oil [11] and limonene [12] are transferred to mask using impregnation method.Tese processes could alleviate the discomfort caused to the skin by the masks and maintain a pleasant scent of limonene within the masks.Numerous studies have explored the permeability and irritationreducing properties of liposomes [13][14][15].Liposomes operate with a mechanism that facilitates the deeper penetration of substances into the skin while preventing small molecules from entering the circulatory system.In the context of minimizing skin irritation, liposomes can decrease the chance of such reactions.Tis is because the substances are stored within the liposomes, preventing direct contact with the skin and consequently averting irritation.
Te development of HC-VitB3 serum using liposomes is promising and provides better user appeal, as it efectively reduces the fshy odor of collagen, enhances its color, improves permeability, and reduces skin irritation.Tis research involves a comparative study between the newly developed HC-VitB3 liposome serum and conventional HC-VitB3 serum formulations, covering various aspects such as odor, color, skin permeability, and product satisfaction as evaluated by volunteers.

Preparation of HC-VitB3
Liposomes.Te HC-VitB3 liposome was prepared using a modifed ethanol injection method [14].To briefy describe the process, each material was carefully weighed and placed into two separate containers: one for the water phase and another for the lipid phase, with ethanol serving as the solvent.Te temperature of both phases was maintained at 60 °C before mixing them together.Subsequently, the ethanol was removed using a rotary evaporator at 50 °C to form the liposome.HC and VitB3 were fxed at 2.0% (w/v) in the formulations.CHOL, SPC, and water were the primary components of the liposomes [16].Te concentrations and ratios of all components are shown in Table 1.

Physical Properties of HC-VitB3 Liposomes.
HC-VitB3 liposomes were evaluated for color and appearance through visual assessment.In addition, a smelling test for the formulations was conducted by a formulator with permission from the Ethics Committee of the Faculty of Pharmaceutical Sciences at Prince of Songkla University, Tailand, which approved this study before its execution.Te assessment involved grading on a scale of fve levels 2 Scientifca represented by plus symbols (+ to +++++), and comparisons were made against a HC-VitB3 solution.Te screening results of physical properties were used to select HC-VitB3 liposomes for further investigation.Te selected formulations had their color determined using a CM 700d spectrophotometer (Konica Minolta, Inc., Tokyo, Japan).Color parameters (CIELAB) L * (0 � black, 100 � white), a * (+ value � red, −value � green), and b * (+ value � yellow, −value � blue) were determined for studying the color of formulations.Total diference in color (ΔE * ) between the HC-VitB3 liposome formulation and the HC-VitB3 solution was calculated using the following equation [4]: where ΔL * , Δa * , and Δb * are the diferences between the corresponding color parameter of the HC-VitB3 liposome and that of HC-VitB3 solution.

Determination of Vesicle Size, Size Distribution, and
Zeta Potential.Te vesicle size, size distribution, and zeta potential of the formulations were assessed at 25 °C using a zeta potential analyzer (Model ZetaPALS, Brookhaven Instrument, Corp, New York, USA).For each measurement, 10 μl of the samples were dispersed in 4 ml of Milli-Q water.All measurements were conducted in triplicate and are reported as mean ± standard deviation [16].

Determination of Entrapment Efciency.
Two methods were used for the determination of entrapment efciency in liposomes, based on the characteristics of the active substances.Tis was due to the presence of two types of active substances: HC and VitB3.
In case of VitB3, each prepared liposome (5 ml) was centrifuged at 24,000 rpm, 4 °C for 2 hours using an ultracentrifuge (Optima ™ L-100XP, Beckman, USA).Ten, the supernatant was analyzed using ultraviolet visible (UV) spectroscopy to measure the amount of free VitB3 in the formulations (F).Te total amount of VitB3 was measured after breaking the vesicles with triton X-100 at a ratio of 1 : 1 of sample and triton X-100 in the formulation (T).VitB3 content in formulation was measured using a modifed UV spectrophotometer method [17].Five solutions (10-50 μg/ ml) of diferent concentrations were prepared from the standard stock solution of VitB3 for linearity study.Te absorbance of these solutions was observed against distilled water as blank at 254 nm, and the obtained data were used for plotting the calibration curve.
In case of HC, encapsulation efciency was evaluated as the percentage diference between the free HC (F) and the total HC (T).Te amount of HC in the solution was determined using a ninhydrin assay, which is widely used for the quantifcation of amino acids.Te procedure was slightly modifed based on the previously published protocol by Moore and Stein [18].In brief, either 20 μl of free HC or total HC phase was mixed with 300 μl of 10% Triton X-100 and vortexed to obtain a homogeneous solution.Ten, 50 μl of 2% ninhydrin in absolute ethanol was added, and this mixture was heated for 5 min at 95 °C, and cooled down to 25 °C.Te Ruhemann's purple formed by the reaction was measured at 570 nm.Te concentration of HC in the sample was calculated by referring to the HC standard curve.Blank liposome was included as a negative control.Te percent entrapment efciency (%EE) was calculated using the following equation [14]: where % EE is the percent entrapment efciency, T is the total amount of VitB3/or HC in the formulation, and F is the free VitB3/or HC amount.

Determination of Vesicle Morphology.
A scanning electron microscope (SEM) was utilized to examine the morphology of liposome vesicles.Sample preparation for SEM assessment followed the method described by Lujan et al. in 2019 [19].A 2% w/v solution of osmium tetroxide in phosphate bufer solution (PBS) was used as a negative lipidtargeting stain fxation solution.Subsequently, it was essential to sputter-coat these samples with a 20 nm thick layer of iridium to eliminate electron charging before acquiring SEM images (JSM5800LV, JOEL, Japan).Scientifca identifed by NIST17 library and Wiley 10 and NIST14 libraries with match factor criteria >90%.USA) and antibiotics (100 U penicillin and 100 U/ml streptomycin, Gibco ® , USA) under 5% CO 2 at 37 °C.Te medium was changed every alternate day.When the cells reached confuence, they were harvested using 0.05% trypsin-EDTA (Gibco ® , USA), followed by the addition of fresh culture medium to create a new single cell suspension for further incubation [21,22].

Cell Viability Assay.
Te human skin fbroblast cell lines (BJ) and human skin keratinocyte cell line (HaCat) at a concentration of 1 × 10 5 cells/ml were seeded into a 96-well plate in complete media.After 24 h, the samples (blank liposome, HC-VitB3 solution, and HC-VitB3 liposome) of various concentrations (19.5, 39, 78, 156, 312, 625 μg/ml, 1.25, and 2.5 mg/ml) in fresh medium were added into the culture plates, and cells without a sample was served as a control.After incubation for 24 h, 3-(4, 5-dimethylthiazolyl-2-yl)-diphenyl-tetrazolium bromide (MTT) solution (5 mg/ml) assay was performed to evaluate cell activity.In brief, the cells were treated with 80 μl of fresh media along with 20 μl of MTT solution and incubated at 37 °C under 5% CO 2 for 4 h.Tereafter, media containing MTT was removed, and 100 μl of DMSO was added.Te absorbance was determined by a microplate reader (Biohit 830, Biohit ® , Helsinki, Finland) at a wavelength of 570 nm.Te percentage of cell viability was calculated and compared to control [5,21,22].

3.4.3.
In Vitro Scratch Assay.Te spreading and migration capabilities of human skin cells were assessed using a scratch assay (injury to the cell monolayer) that measured the expansion of cell population on a surface.Te BJ and HaCat cells line at a concentration of 1 × 10 6 cells/well in complete media were seeded in a 12 well plate.Once the confuent monolayer was formed, a linear scratch was generated in the monolayer with a sterile pipette tip.Any cellular debris was removed by washing with phosphate bufer saline (PBS) and replaced with 2 ml of samples.Te complete media without sample served as a control.Photographs were taken at a 10× magnifcation using a microphotograph (Olympus CK2, Japan) on day 0, after which the plates were incubated at 37 °C with 5% CO 2 , and photographs were taken at days 1 and 2. Te images acquired for each sample were further analyzed quantitatively by using computing software (ImageJ/Java).By comparing the images from days 0-2, the distance of each scratch closure was determined and the percentage migration rate was calculated.Average of left scratch and right scratch were taken separately.Percent migration was calculated for left scratch and then right scratch using the following equation: %Migration rate � average distance between scratch(day 0) − average distance between scratch(day 1) average distance between scratch(day 0) × 100.
Samples were measured in quadruplicates.Percent rate of migration obtained from all four wells were averaged and recorded [22].

Determination of Soluble Collagen Production.
Te human skin fbroblast BJ cell line at an initial concentration of 1 × 10 5 cell/well was seeded in a 96-well plate.After 24 h, the samples of various concentrations in fresh medium were added into the culture plates, respectively.After incubation for 24 h, the supernatants were collected.Ten, the total amount of soluble collagens was assayed using the Sorcol ® collagen assay kit (Biocolor Ltd., UK).In brief, 100 μl of experimental cell supernatant was mixed with 200 μl of dye solution and mixed gently at room temperature for 30 min.After that the samples were centrifuged at 15, 000g for 10 minutes to form a pellet of collagen.Te supernatant was removed and the produced soluble collagen was dissolved by 500 μl of alkali reagent.Te resultant solution from alkali reagent was transferred to the 96-well plate and the absorbance was determined by a microplate reader at a wavelength of 540 nm.Te amount of collagen was calculated based on a standard curve of soluble collagen [22].

In Vitro Skin Permeation of HC-VitB3
Liposome.Skin permeation study of the selected HC-VitB3 liposome and HC-VitB3 solution was carried out using a modifed Franz 4 Scientifca difusion cell (Model Hanson 57-6M, California, USA).Pig ear skin that was used as the skin model was provided by a pork butcher (local market in Hat Yai, Tailand); it was mounted between the donor and receptor compartments [16,23].HC and VitB3 (2% w/v) liposome and HC-VitB3 solution (2 ml) were placed on the skin covered by the upper compartment of a Franz difusion cell.Te samples (2 ml) were withdrawn at 0.5, 1, 2, 4, 8, 16, and 24 h from the receptor chamber and immediately replaced with an equal volume of fresh receptor medium (PBS pH 7.4).Te content of VitB3 in receptor fuid was analyzed by a UV spectrophotometer.Five concentrations of VitB3 solution in PBS (1-5 μg/ml) were prepared for linearity study.Te permeation profle was plotted between cumulative amount of VitB3 permeated per unit area and function of time.Te cumulative amount (Q t ) of VitB3 permeation per unit area was calculated using the following equation: where Q t is the cumulative amount of VitB3 permeated per unit area of the skin (μg/cm 2 ), C n is the concentration of VitB3 measured at No. n sampling interval (μg/ml), C i is the concentration of VitB3 measured at No. i sampling interval (μg/ml), V is the volume of individual Franz difusion cell (ml), S is the volume of sampling aliquot, and A is the effective difusion surface area, 1.77 cm 2 [16,23].

Deposition of HC-VitB3
Liposome in the Skin.After completing the in vitro permeation study (24 hours), the amount of VitB3 accumulated in the skin was analyzed [24].Te skin was removed from the difusion cell, cut into small pieces, and put into a centrifuge tube containing 5 ml of methanol.Subsequently, it was vortexed for 2 minutes, sonicated for 15 minutes, and then centrifuged at 10,000 rpm (4 °C for 10 minutes).Finally, the supernatant was analyzed for VitB3 content using UV spectrophotometer.

Preparation of HC-VitB3
Liposome Serum.HC-VitB3 liposome serum and HC-VitB3 serum were prepared by mixing all the ingredients in water.For preparation of the HC-VitB3 serum, each ingredient, such as disodium EDTA, HC, VitB3, polysorbate 20, propylene glycol, and phenoxyethanol was added to the water and continuously stirred until a clear solution was obtained.On the other hand, for preparing the HC-VitB3 liposome serum, the same preparation ingredients in same concentrations as in HC-VitB3 serum was added to a liposome suspension containing HC and VitB3.Ten, sodium carboxymethyl cellulose 0.5-1.0%w/v was added to both solutions to increase the viscosity of the formulations [25].

Characterization of HC-VitB3 Liposome Serum.
Te physical properties of HC-VitB3 liposome serum and HC-VitB3 serum were assessed visually, including color and appearance, and photographs were taken.Color determination of both formulations was done using a CM 700d spectrophotometer (Konica Minolta, Inc., Tokyo, Japan).Total diference in color (ΔE * ) between the HC-VitB3 liposome serum and the HC-VitB3 serum was calculated using equation ( 1) [4].pH of formulation was measured by a pH meter (Mettler Toledo pH510), and viscosity was measured by Brookfeld viscometer DV-III ultrarheometer with a LV spindle.Both pH and viscosity were measured at 25 °C in triplicate [25].
3.9.Product Satisfaction Assessment.Tis study received prior approval from the Ethics Committee of the Faculty of Pharmaceutical Sciences at Prince of Songkla University, Tailand (MHESI 68108/2722).Informed consent was obtained from all volunteers before their participation in the study.Te satisfaction assessment was a comparative study using the same tester to test each product with a doubleblind study.Terefore, equation ( 5) [26] was used to calculate the minimum number of participants to ensure reliable results for product satisfaction assessment.Inclusion criteria were as follows: the minimum number of volunteers required was at least 46 healthy male or female, who were aged between 21 and 70 years, willing to agree to the product assessment testing protocols, sign the informed consent, and did not have any skin disease.Exclusion criteria were as follows: having histories of allergies from natural ingredients or chemicals contained in the HC-VitB3 liposome serum and HC-VitB3 serum formulation [25].Testing was conducted by having volunteers apply the product to the forearm area, assess the odor, and observe the various characteristics of both the products.Te assessment included evaluating the satisfaction with regard to smell, color, texture, and skin absorption.Te volunteers were not informed about which products were HC-VitB3 serum and HC-VitB3 liposome serum.Te evaluation process took 30 minutes and utilized the abovementioned criteria to measure satisfaction levels, employing a Likert scale.Te characteristics were determined using a 5-level rating scale, which includes the highest (5), high (4), moderate (3), low (2), and the lowest (1) levels of satisfaction.At the end of the evaluation, volunteers selected their preferred products and provided the reasons.
where n is the required sample size, Z α is 1.96 when α � 0.05, Z β is 1.28 when β � 0.10, σ is standard deviation, σ 1 is standard deviation of testing product 1, σ 2 is standard deviation of testing product 2, r is 0 for getting the greatest number of sample size, and d is the diference in means of satisfaction score.

Statistical Analysis.
Te data were expressed as the mean ± SD, and the statistical analyses were conducted using either one-way ANOVA or a t-test, depending on the data evaluation.Color evaluation of HC-VitB3 liposomes and HC-VitB3 solution was analyzed using one-way ANOVA.
Cell proliferation, migration of human fbroblast, soluble Scientifca collagen production, skin permeation, and skin deposition of HC-VitB3 liposome were analyzed using t-test.Physicochemical properties and product satisfaction of HC-VitB3 liposome serum and HC-VitB3 serum were analyzed using ttest.Te statistical diferences between values showing P < 0.05 were considered as signifcant.
Ten formulations of liposomes containing HC-VitB3 with varying ratios of SPC: CHOL: Tween 80/Span 80 were prepared.Te selection criteria were based on physical characteristics, such as their ability to mask odors, and color of freshly prepared samples compared to HC-VitB3 solution samples as well as all samples after one week (Table 2).Once the suitable formulations were identifed from Table 2, an evaluation was conducted to determine the color, particle size, polydispersity index (PDI), zeta potential, and percentage of entrapment efciency in order to select the appropriate formulation.
Te results shown in Table 2 revealed that the HC-VitB3 solution exhibited a clear gray color and emitted a very strong fshy odor when compared to all of the HC-VitB3 liposomes.However, HC-VitB3 liposomes F1 and F3, after being stored for one week, emitted a stronger fshy odor than their freshly prepared counterparts.Terefore, these two formulations were eliminated due to not meeting the selection criteria.Eight formulations of HC-VitB3 liposomes underwent assessment for particle size, polydispersity index (PDI), zeta potential, and percentage of entrapment efciency, as displayed in Table 3. Te color of these formulations is shown in Table 4.
All eight formulations of HC-VitB3 liposomes were nanosized ranging from 161 to 344 nm, exhibited low PDI values (0.1-0.3), and possessed zeta potential values ranging from −19 to −41 mV.Te formulation with Tween 80 had a smaller particle size compared to the one with Span 80.All liposomes exhibited a negative value of zeta potential, primarily attributed to the negative charge of the phosphate group in phosphatidylcholine.Zeta potential serves as an indicator of the physical stability of liposomes [9].Te particle size tends to impact the charge distribution on the liposome surface [27].Interestingly, each Span 80-based formula not only exhibited a larger size compared to the Tween 80 formula, but also featured a higher negative zeta potential value.Tis distribution of negative charges on the liposome surface results in repulsion between particles, reducing the likelihood of agglomeration or particle collision [9].PDI is a measure of particle size distribution, indicating the variations in particle sizes within a sample.Liposomes with consistent particle sizes exhibit a low PDI [28].Tus, favorable physical properties of liposomes include minimal particle size variation and a high zeta potential.In addition, a high percent entrapment efciency is an essential characteristic of preferable liposome formulations.HC-VitB3 liposome formulations F2 and F4 exhibited the highest percent entrapment efciency of VitB3 (95.31% and 95.73%, as shown in Table 3), which corresponds to their ability to mask the fshy odor, as indicated by the results in Table 2. Te entrapment efciency of HC in all eight formulations was in the range of 4.66-49.63%,which corresponds to the result of VitB3 entrapment.HC-VitB3 liposome formulation F4 gave the highest percent entrapment efciency (49.63 ± 1.74%).However, the HC entrapment value in the F4 liposome formulation was still half of the VitB3 value.Te efciency of substance entrapment in liposomes is infuenced by the proportions of various components.Liposomes contain cholesterol, which contributes to strengthening the liposome wall and maintaining its shape.However, when cholesterol levels surpass a specifc threshold, they can disrupt the double-walled structure of liposomes, resulting in reduced substance entrapment efciency [29].Moreover, surfactants present in the liposome formula, such as Tween 80 or Span 80, have the potential to degrade the skin membrane and facilitate alterations in the shape of liposome bilayers, making them more suitable for their intended purpose [16].Te entrapment efciency of the formulation is afected by the size of the active substance molecule, especially when comparing HC with a molecular weight (MW) of 102-10175 Da to VitB3 with a MW of 122 Da.Furthermore, the solubility of VitB3 in aqueous solutions is higher than that of HC, which allows liposomes to encapsulate VitB3 much more efciently than HC.Tis corresponds to the fndings of the review by Eloy et al. [30].In Table 4, the color values of both the HC-VitB3 solution and HC-VitB3 liposomes reveal that the L * value of HC in every formula of liposomes was signifcantly higher than that of the HC-VitB3 solution (P < 0.05), indicating an increased brightness value for the HC-VitB3 liposomes.When calculating the total color diference value (∆E) by comparing it with the HC-VitB3 solution, it was observed that each HC-VitB3 liposome formulation had a signifcantly diferent ∆E value (P < 0.05).Tis indicates that the liposome preparation reduced the grayness of the collagen, with the external color being attributed to the phospholipids.Te color value is infuenced by the ingredients composing the liposomes [31].
Based on the criteria for selecting HC-VitB3 liposomes, both F2 and F4 were the most efective formulations for encapsulating substances.When evaluating the color difference between HC-VitB3 liposomes and the HC-VitB3 solution, it was observed that formula F4 yielded the highest ∆E value, resulting in a bright yellow color formulation.Terefore, F4 was chosen as the optimal formulation for testing skin penetration and its efectiveness in masking the fshy odor when compared to the HC-VitB3 solution.Furthermore, morphology of HC-VitB3 liposome (F4) was determined by SEM is shown in Figure 1.
Te morphology of HC-VitB3 liposomes, as revealed in SEM photographs, shows spherical vesicular structures.Te size of the vesicles corresponded to the particle size measurement obtained from the zeta potential analyzer (170 nm).Scientifca found that at 3.2026 minutes, 3.4233 minutes, and 9.3479 minutes, peaks were observed in the HC-VitB3 solution, but they were not present in the HC-VitB3 liposome.Te peak at 3.4452 minutes was identifed as 1-butanol, 3-methyl, a substance known for its unpleasant odor [32].Likewise, the peak at 9.3479 minutes was identifed as 1-undecene, which is also associated with an odor [33].However, the substance responsible for the peak at 3.2026 minutes could not be identifed.Based on these observations, it can be inferred that liposomal-hydrolyzed collagen is efective in reducing the odors caused by 1-butanol, 3-methyl, and 1-undecene present in the HC-VitB3 solution.

Cell Viability of HC-VitB3
Liposome.Te toxicity of blank liposome, HC-VitB3 solution, and HC-VitB3 liposome was assessed in BJ cells and HaCaT at concentrations ranging from 19.5 μg/ml to 2.5 mg/ml.As depicted in Figure 3, it was observed that at every concentration ratio of HC-VitB3 liposome, the percentage cell survival values in BJ and HaCaT cells did not difer signifcantly from those in the control group.However, both the blank liposome and the HC-VitB3 solution exhibited signifcantly lower cell viability percentages compared to the control group.In the BJ cell test, at a concentration ratio of 1 : 8 (2.5 mg/ml), the percentage cell survival values of blank liposome and HC-VitB3 solution were 82.88 and 80.79, respectively.In the HaCaT cell test, the cell survival percentage of blank liposome signifcantly reduced to below 60 percent at concentration ratios ranging from 1 : 16 to 1 : 8 (1.25-2.5 mg/ml), whereas the survival percentage of HC-VitB3 solution decreased to 70.85 percent at a concentration of 2.5 mg/ml.Terefore, we can conclude that, in this study, HC-VitB3 liposome does not induce cell toxicity at any concentration.

Efect of HC-VitB3 Liposome on Migration of BJ and
HaCaT Cells.HC-VitB3 liposome afected the cell migration of BJ and HaCaT cells as shown in Figure 4. HC-VitB3 liposomes signifcantly stimulated cell migration compared to the negative control.Te percentage of migration in BJ cells treated with HC-VitB3 liposomes was notably higher than that in the negative control for both cell lines.Specifcally, on day 1, a concentration of 2.5 mg/ml of HC-VitB3 liposomes increased BJ cell migration to 74.80 ± 0.89%, while the negative control exhibited a migration of only 35.24 ± 0.97%.Moreover, a concentration of 2.5 mg/ml of HC-VitB3 liposomes enhanced HaCaT cell migration to 65.94 ± 6.53% compared to the negative control's 45.65 ± 3.90% on day 1.Consequently, HC-VitB3 liposomes demonstrated superior wound healing efcacy compared to the control group (P < 0.05).Tese results confrmed the efective wound healing activity of HC-VitB3 liposome formulation [5].

Soluble Collagen Production of HC-VitB3 Liposome.
Blank liposomes and HC-VitB3 liposomes in various concentrations were used to stimulate collagen production in the BJ cell line and compared to the results of the control.At a concentration of 1.25 mg/ml, only HC-VitB3 liposomes signifcantly increased collagen production in BJ cells, resulting in signifcantly higher amounts (40.92 ± 25.87 μg/ ml) compared to the control (11.34 ± 1.74 μg/ml).Furthermore, when the concentration was increased to 2.5 mg/ml, soluble collagen production reached 256.61 ± 25.89 μg/ml.In contrast, blank liposome did not stimulate collagen production in BJ cells.Tese results revealed that HC-VitB3 liposome exhibited good collagen production activity and was nontoxic to both cells.In addition, HC-VitB3 liposome promoted collagen production in BJ cells in a concentrationdependent manner similar to Jatropha curcas L extract [22].

Skin Permeation and Skin Deposition of HC-VitB3
Liposome.Te skin permeation of HC-VitB3 liposome through pig ear skin was evaluated.Te physiological, biochemical, and histological characteristics of porcine ear skin exhibit many similarities when compared to human skin in terms of lipid position and thickness [34,35].Te in vitro skin permeation profles of HC-VitB3 solution and HC-VitB3 liposome are shown in Figure 5.Among the formulations studied, formulation F4 proved to be the most efective HC-VitB3 liposome in skin penetration when compared to HC-VitB3 solutions.In the experiment, VitB3 served as a representative compound to assess the entrapment and skin penetration of liposomes.Both HC and VitB3 are water-soluble substances and are located within the central cavity of the liposome vesicles.However, the entrapment efciency of HC in F4 liposome was only 49.63% which was lower than VitB3 (95.73%).It was observed that HC-VitB3 liposomes exhibited a signifcantly higher accumulation of VitB3 in the receptor fuid at 0.5, 1, 2, 4, 8, 16, and 24 hours, in contrast to the HC-VitB3 solution (P < 0.05).Tis suggests that HC and VitB3 encapsulated within liposome vesicles can readily traverse the layers of the skin and accumulate in both the epidermis and dermis.Tis capability is due to the lipid bilayer structure, which closely resembles the skin's cell membrane, enabling liposomes to penetrate the cell membrane space and deliver encapsulated substances to their target locations.Moreover, liposomes contain surfactants, such as Tween 80, which can alter the fuidity of the cell membrane.Tis alteration causes denaturation of the cell membrane wall [13], facilitating the enhanced permeation of liposomes into the intercellular spaces.Te formulations of liposomes thus prove advantageous in promoting the absorption of various substances through the skin.Te low permeability of all compounds might be due to the structure of the outermost skin layer, the stratum corneum.It consists of protein-rich corneocytes embedded in a matrix of lipids.Tis domain is the ratelimiting step for the penetration of drugs [36].Analysis of the accumulated amount of VitB3 in the skin revealed that HC-VitB3 liposomes exhibited a value of 1442.67 ± 106.17 μg of VitB3 accumulation in pig skin, which was signifcantly higher than the 1003.37 ± 89.20 μg observed in the HC-VitB3 solution (P < 0.05).Tese results, consistent with numerous studies [13][14][15], indicate that liposomes employ various mechanisms to facilitate skin absorption, enabling substances to penetrate deeper into the skin.can be attributed to the presence of liposome components.
Regarding viscosity, the HC-VitB3 serum had a viscosity of 2,913.33 cPs, while the HC-VitB3 liposome serum exhibited a higher viscosity of 5,400 cPs.Tis increased viscosity is primarily due to the presence of lipids, such as phosphatidylcholine from soybeans and cholesterol.Te viscosity of the serum formulation plays an important role on deciding whether it feels comfortable or not when applied on the skin; furthermore, viscosity depends on the amount of thickening agent [25].In this study, the viscosity of the HC-VitB3 liposome serum was higher than that of the HC-VitB3 serum by almost two times.However, the results showed that the skin permeation value of the liposome was still higher than that of the solution.A balance between viscosity and absorptivity on the skin is one of the many factors that infuence the satisfaction of the product users.Furthermore, the HC-VitB3 liposome serum followed the quality critical attributes such as physical quality and stability of the product as stated in design and development of topical liposomal formulations in a regulatory perspective [38].10 Scientifca in Table 6.Satisfaction scores for texture and absorption did not exhibit signifcant diferences > 0.05) because some volunteers preferred the texture of the HC-VitB3 serum, fnding it lighter and less heavy on the skin.Conversely, some volunteers favored the texture of the HC-VitB3 liposome serum because it provided more moisture after application, resulting in no signifcant diference in texture scores.However, satisfaction with the color of the HC-VitB3 liposome serum product was signifcantly lower than that of the HC-VitB3 serum (P < 0.05).Tis was because volunteers were not shown the color of the serum stored in an opaque bottle.Te color of the serum became apparent only when a small amount was dispensed, leading most volunteers to rate their satisfaction with the color of the HC-VitB3 serum higher than that of HC-VitB3 liposome serum.In terms of scent, satisfaction of volunteers with the HC-VitB3 liposome serum product was signifcantly higher than that of HC-VitB3 serum (P < 0.05).Tis was due to HC-VitB3 liposome   Scientifca efectively masking any fshy odors, allowing the perfume scent to become more prominent.In contrast, the HC-VitB3 serum had noticeable fshy smell, and the applied perfume could not efectively mask it, resulting in an unpleasant scent.All the 100 volunteers reported no irritation after using both the HC-VitB3 serum and HC-VitB3 liposome serum.When volunteers were asked to evaluate the products and select their preferred option, 73 of them chose the HC-VitB3 liposome serum.Most of them cited the scent as a key factor infuencing their choice.On the other hand, 27 people chose the HC-VitB3 serum, appreciating its lighter texture and being less sensitive to the scent.Interestingly, most males chose the HC-VitB3 serum, which is consistent with research showing that males' ability to discriminate diferent odors is poorer than females [39].Some volunteers expressed the opinion that the HC product derived from fsh should have a slightly fshy odor due to certain active substances present in the product.However, the product development concept prioritizes quality and acceptability, so the product should remain stable for a specifed period.Terefore, liposomes were used to incorporate HC for masking odor and enhancing the quality of the cosmetic product.

Potential Cosmetic Applications of HC-VitB3 Liposome
Serum.From results of all the studies, the developed liposome with a proper lipid bilayer structure and ratio has the potential to ofer both efective concealment of fshy odors and unpleasant colors, as well as high skin penetration.Furthermore, HC-VitB3 liposome did not induce cell toxicity and exhibited good collagen production and efective wound healing activity.Te liposome serum was prepared using a concentration of efective ingredients.Te HC-VitB3 liposome serum represents an innovative approach in the feld of cosmetic skincare.Hydrolyzed collagen, a key component of the serum, is known for its ability to replenish and retain moisture in the skin.When combined with VitB3, it forms a potent hydrating complex that penetrates deep into the skin's layers, promoting optimal hydration levels.Tis results in improved skin elasticity and frmness, reducing the appearance of fne lines and wrinkles [14,25].Te combination of HC, VitB3, and liposomes holds immense potential for various cosmetic applications.From enhancing skin hydration and frmness to promoting collagen synthesis and brightening the complexion, this innovative liposome serum ofers multifaceted benefts for skin health and rejuvenation.Further research and clinical studies could highlight its efcacy and establish its position as a valuable product in cosmetic skincare regimens.

Conclusion
HC-VitB3 liposomes can improve the physicochemical properties and reduce the odor and undesirable color of the extract while enhancing absorption through the skin.Utilizing a suitable weight ratio of phosphatidylcholine, cholesterol, and Tween 80 at 8 : 2 : 1 results in the production of nanosized vesicles, which is promising for the development of advanced cosmetic products.Te HC-VitB3 liposome serum also efectively masks fshy odors.Furthermore, none of the 100 volunteers reported experiencing irritation after using both the HC-VitB3 serum and HC-VitB3 liposome serum.In the overall evaluation, a majority of the volunteers selected HC-VitB3 liposome serum as their preferred product.Teir rationale lies in the signifcant impact of scent on the usability of cosmetic products.Tus, it can be concluded that the development of this liposome product elevates the value of HC extracted from salmon fsh (which would otherwise be considered a waste) by turning it into a valuable ingredient in the beauty industry.

4. 7 .
HC-VitB3 Liposome Serum and PhysicochemicalProperties. HC-VitB3 liposome serum was a clear and a bright yellow solution compared to HC-VitB3 serum, as shown in Figure6.Te evaluation of physical properties included color, pH measurement, and viscosity measurement of both formulations and is shown in Table5.Te results of the colorimetric test indicated that the HC-VitB3 liposome serum product exhibited a brighter appearance, as evidenced by a signifcantly higher L * value (P < 0.05), and more pronounced red and yellow hues.Moreover, both the a * and b * values were signifcantly greater (P < 0.05) for the liposomal formulation, which can be attributed to the inherent yellow color of soybeans.Notably, the presence of phosphatidylcholine in liposome walls[37] contributed to a color diference value of 3.05, when compared to the HC-VitB3 serum.Te pH value of the HC-VitB3 serum was 6.94, whereas the pH value of the HC-VitB3 liposome serum was 7.04, indicating a slightly more alkaline nature.Tis diference

Table 2 :
Physical properties of HC-VitB3 liposomes in terms of odor and color comparing to HC-VitB3 solution.
Data are expressed as mean ± SD (n � 3).

Table 6 :
Results of satisfaction assessment among 100 volunteers.Data are expressed as mean ± SD (n � 100).Signifcance values (P < 0.05) are shown in diferent letters in the same row.